Ferritic angular shot
Angular ferritic shot is obtained by crushing spherical shot and is subjected to heat treatments that give it a metallographic structure suitable for the purpose and the highest technicality produced with selected raw materials in modern plants that guarantee constant quality over time. It is obtained by casting and then heat treatment to give it optimal resilience and fatigue resistance.
Standard shot sizes including the chemical-physical analysis are as shown in the table below.
SKU: 43678
Technical data sheets
Additional information
Technical data
| G 120 | G 80 | G 50 | G 40 | G25 |
| 0,075 – 0,300 mm | 0,125 – 0,425 mm | 0,180 – 0,710 mm | 0,300 – 1,00 mm | 0,425 – 1,180 mm |
| G 18 | G 16 | G 1 | G 12 | G 10 |
| 0,710 – 1,400 mm | 1,00 – 1,700 mm | 1,180 – 2,00 mm | 1,400 – 2,360 mm | 2,00 – 2,800 mm |
Chemical analysis
| Carbon content | C | Mn | Si | S | P | Hardness |
| HIGH | ca. 0,50 – 0,80% | ca. 0,40 – 0,70% | ca. 0,10 – 0,50% | ca. < 0,050% | ca. < 0,050% | GL 47 – 56 HRC GP 53 – 60 HRC GH > 65 HRC |